Comparison of Descaling Methods to Study the Corrosion Kinetics of Ferritic Steels after Dynamic Exposure to Molten Carbonates

Number of pages: 20 Posted: 24 Aug 2022
Pauline Audigié, Sergio Rodríguez Catela, Alina Agüero, Fatima Pedrosa, Teresa Paiva and Teresa C. Diamantino
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN and National Laboratory for Energy and Geology
Downloads 39 (1,196,171)

Abstract:

Loading...

Molten salts, Steels, Hot corrosion, Weight Loss, X-Ray diffraction

2.

Corrosion degradation of IN617 after 1000 h of exposure in molten chlorides at 700 °C

Number of pages: 34 Posted: 13 Dec 2025
Alina Agüero, Sergio Rodríguez Catela, Pauline Audigié, Jon Pascual, Gustavo García-Martín and Francisco Javier Pérez
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, Universidad Complutense de Madrid (UCM) and Universidad Complutense de Madrid (UCM)
Downloads 38 (1,249,711)

Abstract:

Loading...

molten chloride, thermochemical energy storage, corrosion, Ni alloy

3.

Corrosion degradation of slurry aluminized IN617after 1000 h of exposure in molten chlorides at 700 °C

Number of pages: 38 Posted: 13 Feb 2026
Alina Agüero, Sergio Rodríguez Catela, Pauline Audigié, Jon Pascual, Gustavo García-Martín and Francisco Javier Pérez
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, Universidad Complutense de Madrid (UCM) and Universidad Complutense de Madrid (UCM)
Downloads 9 (1,555,090)

Abstract:

Loading...

Molten chlorides, corrosion, slurry aluminide coatings, CSP, energy storage