default author photo

Xiaochao Jin

affiliation not provided to SSRN

  • affiliation not provided to SSRN

SCHOLARLY PAPERS

6

DOWNLOADS

156

TOTAL CITATIONS

3

Scholarly Papers (6)

Actions:
Email selected abstracts
1.

Investigation on Aging Behavior and Failure Mechanism of Blast-Resistant Polyurea Coating in Service Environments

Number of pages: 25 Posted: 30 Nov 2024
Peng Zhang, Zhijun Wang, Jianping Yin, Menghao Wang, Wenqian Hao, Ximei Wen, Baozhu Wang and Xiaochao Jin
North University of China, North University of China, North University of China, North University of China, North University of China, affiliation not provided to SSRN, affiliation not provided to SSRN and affiliation not provided to SSRN
Downloads 34 (1,277,121)

Abstract:

Loading...

Polyurea coating, Blast resistance, Environmental aging, Mechanical performance, Failure mechanism

2.

Thermo-Mechanical Analysis of Tbc-Film Cooling System Under High Blowing Ratio Considering the Effects of Curvature

Number of pages: 37 Posted: 12 May 2023
Linchuan Liu, Shunguo Fu, Zhongwei Hu, Jian Wu, Jian Chen, Xiaochao Jin and Xueling Fan
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN and affiliation not provided to SSRN
Downloads 34 (1,277,121)

Abstract:

Loading...

thermal barrier coating, Film cooling, Thermo-mechanical analysis, Substrate curvature, High blowing ratio

3.

Cyclic Thermal Shock Behaviors and Failure Mechanisms of Eb-Pvd Thermal Barrier Coating Under Radiant Heating

Number of pages: 20 Posted: 23 Jan 2023
Wei Gao, Pan Li, Xiaochao Jin, Jinchao Zhao, LaiXia Yang and Xueling Fan
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN and affiliation not provided to SSRN
Downloads 28 (1,345,526)

Abstract:

Loading...

Thermal barrier coating, cyclic thermal shock, thermally grown oxide, failure mechanisms, thermal mismatch stress.

4.

Oxidation and Interdiffusion Behaviours of Nicocralyhf Coating on a Nickel-Based Single Crystal Superalloy at 1050℃

Number of pages: 28 Posted: 20 Dec 2023
Jierui Wang, Xiaochao Jin, Pan Li, Kun Xiong, Jiaping Li, Ziang Li, Cheng Hou and Xueling Fan
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN and affiliation not provided to SSRN
Downloads 24 (1,411,822)

Abstract:

Loading...

Thermal barrier coating system, NiCoCrAlYHf coating, Nickel-base single crystal superalloy, oxidation, interdiffusion

5.

High Temperature Fatigue Behaviors of Coated and Uncoated Nickel-Based Single Crystal Superalloys Dd6: Microstructures Evolution, Damage Mechanisms and Lifetime Prediction

Number of pages: 32 Posted: 16 Jul 2024
Jiaping Li, Xiaochao Jin, Dongxu Li, Jingjing Yang and Xueling Fan
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN and affiliation not provided to SSRN
Downloads 21 (1,436,435)
Citation 3

Abstract:

Loading...

Nickel-based single-crystal superalloys, Thermal barrier coating, Isothermal fatigue, Fatigue lifetime, Damage mechanism

6.

Residual Stress Evolution and Failure Behaviour of High-Temperature Radar-Infrared Compatible Stealth Coatings Under Thermal Cycle Loads Considering the Interface Morphology

Number of pages: 31 Posted: 18 Aug 2025
Wei Pi, Shengnan Fu, Rong Ma, Xianglian He and Xiaochao Jin
affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN, affiliation not provided to SSRN and affiliation not provided to SSRN
Downloads 15 (1,526,714)

Abstract:

Loading...

Radar-infrared compatible stealth coating, residual stress, Thermal cycle, Interface morphology, Thermally grown oxide