Ordered Mesoporous Carbon Fiber Bundles with High-Density and Accessible Fe-Nx Active Sites as Efficient Orr Catalysts for Liquid and Flexible Zn-Air Batteries

Abstract

Fe-NX/C electrocatalysts have aroused extensive interest in accelerating sluggish oxygen reduction reaction (ORR) kinetics as potential alternatives to platinum catalysts in rechargeable Zn-air batteries (ZABs). However, the low density and poor accessibility of Fe-NX sites have severely restricted the electrocatalytic performance of Fe-NX/C. Herein, Fe, N co-doped ordered mesoporous carbon fiber bundles are prepared through a ligand-assisted strategy with nitrogen-rich 1,10-phenanthroline as space isolation agent. 1,10-phenanthroline reveals a six-membered heterocyclic structure containing abundant nitrogen species to tightly coordinate with Fe ions, which is conducive to achieving high-density Fe-NX sites. Meanwhile, the adoption of SBA-15 as hard-templates enables the catalysts with highly ordered channels and large specific surface areas, improving the accessibility of Fe-NX sites. The optimal PDA-Fe-900 catalyst demonstrates a positive half-wave potential of 0.84 V in alkaline solution, outperforming the commercial Pt/C (0.83 V). In addition, PDA-Fe-900 delivers comparable ORR performance to commercial Pt/C in acidic electrolyte. Impressively, when PDA-Fe-900 is employed as an air cathode, it achieves large power densities of 163.0 mW cm−2 in liquid-state ZAB and 116.6 mW cm−2 in the flexible solid-state ZAB. This work provides an efficient ligand-assisted pathway for fabricating catalysts with dense and accessible Fe-NX sites as high-performance ORR electrocatalysts for ZABs.

Keywords: oxygen reduction reaction, ordered mesoporous carbon, high-density Fe-NX sites, accessibility, Zn-air battery