Cobalt Based Bimetallic Catalysts for Heterogeneous Electro-Fenton Adapting to Vary Ph for Hedp and Mit Degradation

Abstract

Most of the materials studied as catalysts in the electro-Fenton system are variants of iron oxide or iron hydroxide. However, iron-based catalysts often exhibit weak catalytic capabilities under neutral and alkaline conditions. In this work, we synthesized three cobalt based bimetallic oxides, Co2CuOx, Co2AlOx, and Co2NiOx, using hydrothermal method and evaluated them as catalysts for the heterogeneous electro-Fenton system to remove HEDP and MIT. Co2NiOx has the highest catalytic degradation activity for HEDP, and Co2CuOx has the best catalytic degradation effect for MIT. Based on characterization results of the catalysts, the reasons for the differences in the pollutant removal efficiency were analyzed, and the optimal pH for the three cobalt based oxides to remove HEDP and MIT was investigated. The results showed that the optimal pH values of the three cobalt based bimetallic oxides are not only influenced by the second metal type, but also by the properties of pollutants. Therefore, suitable cobalt based catalysts can be selected based on the different properties of pollutants, or the composition of cobalt based catalysts can be adjusted to meet the different pH requirements of target wastewater. The three cobalt based bimetallic oxides exhibited good degradation of HEDP and MIT under neutral conditions, which to some extent solved the problem of narrow pH range in the practical application of the electro-Fenton process.

Keywords: Electro-Fenton, cobalt based bimetallic oxide, methylisothiazolinone, 1-hydroxyethylidene-1, 1-diphosphonic acid